Download Full DatasheetPDF Datasheet

A350 LF2 / A105 Carbon Steel

ASTM A350 LF2 / A105 steel stockholders and suppliers throughout the UK. This carbon steel grade is available as full bar lengths or cut pieces in round bar. It is commonly supplied in the as rolled or normalised condition. A350 LF2 has medium strength and impact characteristics and is a readily weldable grade of steel. Machinability is similar to other low carbon steels such as 070M20, S275 and S355. This grade is used in a wide range of industries where components require service at low temperature.

A350 LF2 steel is held on stock and can be delivered throughout the UK.  All orders are supplied in accordance with our ISO 9001 accreditation.

Alternative carbon steel grades we supply  EN3 | EN8 | EN9 | EN32 |  EN43|  070M20 | 080M40 | 070M55 | 080A15 | S275 | S355  |  Key Steel | C45

Form of Supply

West Yorkshire Steel are steel stockholders and suppliers of ASTM A350 LF2 / A105 carbon steel in round bar. Diameters and flat bar can be sawn cut to your exact requirements. Ground steel bar can be supplied, providing a precision ground steel bar to tight tolerances.

Click here to contact our experienced sales team who will assist you with your enquiry.

  • Diameter

Click on the headings below for further information

Applications

A350 LF2 is used in a wide range of industries such as the petrochemicals, oil and gas sectors.  This grade is commonly used in the manufacture of flanges and fittings.

Carbon 0.30% max Manganese 0.60-1.35%
Silicon 0.15-0.30% Sulphur 0.040% max
Phosphorous 0.035% max Chromium 0.30% max
Nickel 0.40% max Molybdenum 0.12% max
Vanadium 0.08% max Niobium 0.02% max
Copper 0.40% max

Preheat the component carefully, then raise the temperature to 900 to 1200°C for forging. To avoid scaling soak time should be kept to a minimum. After forging cool slowly, preferably in a furnace.

Heat the steel slowly to 860-930°C, soak well. Air cool.

Heat slowly to 890-960°C and allow it to be heated through. Quench in water.

Temper the A350 LF2 steel component immediately after quenching whilst still hand warm. Re-heat to the tempering temperature then soak for one hour per 25 millimetre of total thickness (2 hours minimum) Cool in air. For most applications tempering of A350 LF2 will be at about 590°C.

We recommend you contact your welding consumables supplier who should provide you full assistance and information on welding A350 LF2 steel.

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each A350 LF2 steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of A350 LF2 carbon steel.

ASTM A350 LF2 / A105 carbon steel is available with a BS EN 10204 3.1 mill certificate, please request when placing any orders.

ASTM A350 LF2 / A105 is supplied in accordance with our ISO 9001:2015 registration.